Heat shrink marker, thermal transfer print, continuous, 18.0mm/6.0mm, black, 26m
Art.-No. 553-31852 | TCGT18-6BK-PO-X-BK | 세부

More products in this product group:

Application	TCGT is a commercial grade 3:1 heat shrink marker material supplied as a continuous tube and printable on both sides. TCGT’s polyolefin compound has good mechanical strength and resistance to organic solvents and chemicals. The surface of the tubing has been especially prepared so that print performance is excellent at all times. HellermannTyton's printer range allow users to create a high quality print. In addition it is possible to either perforate the tubing at pre-determined lengths or fully sever the markers.
Articolo	TCGT18-6BK
Colore	Nero (BK)
Con adesivo interno (Si/No)	No
Cont. conf.	26m
Descrizione Breve	Marcacavo termo 3:1 26m TCGT18-6BK
GLOBAL PART DESCRIPTION	TCGT18-6BK-PO-X-BK
Materiale	Poliolefina reticolata (PO-X)
org.mozilla.javascript.Undefined@0	ASTM D638
Quantità per	cartone
Variante	Parete sottile
org.mozilla.javascript.Undefined@0	ASTM D2671
Test invecchiamento termico	168h/175°C
org.mozilla.javascript.Undefined@0	Sì
Prodotto: Categoria	Marcacavi termorestringenti a guaina continua, trasferimento termico
Prodotto: Famiglia	TCGT - 3:1 qualità commerciale
Rapporto di restringimento	3:1
Test shock termico	4h/250°C
Utensile	H6100, TT431, TT4030, TT4030DS

org.mozilla.javascript.Undefined@0	No
Allungamento alla rottura	300 %
Assorbimento acqua	0.20%
Carico di rottura	11.00N/mm²
Certificazioni
Certificazioni	C22.2 no. 198.1-99
Classe di isolamento	B (VDE 0530)
Conformità RoHS	Sì
Resistitività dielettrica	10¹⁶ Ω cm
Ribbon consigliato	TTDTHOUT, TTRW, TT822OUT8
Rigidità dielettrica	20kV/mm
Temp. di esercizio - °C	da -55 °C a +135 °C
Temp. min restringimento - °C	+90 °C
UL Listed	No
org.mozilla.javascript.Undefined@0	continuo
Zero Alogeni	No
org.mozilla.javascript.Undefined@0	ASTM D638
org.mozilla.javascript.Undefined@0	ASTM D638
org.mozilla.javascript.Undefined@0	ASTM D2671
org.mozilla.javascript.Undefined@0	ASTM D257
org.mozilla.javascript.Undefined@0	SI