Heat shrinkable tubing up to 3:1 - 1 m lengths
Art.-No. 319-30100
| TREDUX Starter Kit-PO-X-BK/YE
|
Copied
This product is not available anymore.
- Thin wall, flexible, cross-linked polyolefin tubing
- 1m shrink tubing lengths delivered in handy display carton
- 9 sizes from 1.5 mm to 101.6 mm
- All tubings can be sold in single 1 meter length or entire box
Request quote
More products in this product group:
| Application | TREDUX thin wall heat shrink tubing is used for general electrical insulation and mechanical protection of cables and wires. |
| Behaviour at Heat Shock | not fluid, not dripping, not cracking |
| Behaviour at low Temperature test method | UL 224 |
| Colour | Black (BK), Yellow (YE) |
| Elongation At Heat Aging | 400% |
| Heat Aging Test | 168h/175°C |
| Heat Shock Test | 4h/250°C |
| Heat shock test test method | UL 224 |
| Material | Polyolefin, cross-linked (PO-X) |
| Minimum Tensile Strength At Heat Aging | 11MPa |
| PART DESCRIPTION | TREDUX Starter Kit-PO-X-BK/YE |
| Pack Content | 1pc. |
| Package Content packed in | pcs. |
| Printable | No |
| Product Family | TREDUX - thin wall |
| Product Group | Heat shrinkable tubing up to 3:1 - 1 m lengths |
| Shrink Ratio | up to 3:1 |
| Type | TREDUX Starter Kit |
| Variant | Thin-Wall |
| Voltage range | 600 V |
| With inner glue (Yes/No) | No |
| Copper corrosion | tested according to UL 224 |
| Dielectric Strength | 20kV/mm |
| Dielectric Strength test method | IEC 60243 |
| Elongation at break (min.) | 6% |
| Elongation at break test method | ASTM D2671 |
| Flammability | UL 224 VW-1 |
| Insulation Class | B (VDE 0530) |
| Min. Shrink Temperature - °C | +70 °C |
| Operating Temperature | -55 °C to +135 °C |
| ROHS compliant | Yes |
| Specifications |
|
| Tensile Strength | 14MPa |
| Test Method Tensile Strength | ASTM D2671 |
| UL File link | Link Link |
| UL Listed (US and Canada) | No |
| UL Recognized (US and Canada) | Yes |
| UL-File Number | E143529 |
| Volume Resistance | 10¹⁴ Ω cm |
| Volume Resistance test method | IEC 93 |
| Water Absorption | 0.2% |